本技術揭示一種無基材乾式可撓性膜電極成型技術，無需使用傳統濕式塗佈所需之有機溶劑及長時間高溫乾燥程序，即可製備具高面密度、膜厚可調及良好可撓曲特性之電池膜電極。透過乾式混料與成膜製程，可有效降低製程能耗與碳排放，並提升電極密度與結構設計彈性，展現低碳、高產率之電極製造優勢。

Abstract

This technology reveals a substrate-free dry forming process for flexible film electrodes. Without the use of organic solvents or prolonged high-temperature drying required in conventional wet-coating processes, the technology enables the fabrication of battery film electrodes with high areal mass loading, adjustable thickness, and excellent flexibility. Through dry mixing and film-forming processes, manufacturing energy consumption and carbon emissions can be effectively reduced, while greater flexibility in electrode density and structural design can be achieved, offering a low-carbon and high-throughput approach to electrode manufacturing.

技術規格

一種無基材乾式可撓性膜電極，膜厚≥ 300 μm，活性材料面密度 ≥ 30 mg/cm²。

Technical Specification

A substrate-free,dry-processed flexible film electrode having a thickness of ≥ 300μm and an active-material areal loading of ≥ 30 mg/cm².

技術特色

主要透過物理混摻、機械壓延及乾式成膜製程，形成具高面密度、可撓曲及膜厚可調之軟式膜電極，相較傳統濕式製程可減少有機溶劑使用與高溫烘烤程序，達到低能耗及低碳製程效益。目前膜電極活性材料面密度可達35mg/cm²，完成組裝之對稱式鈕扣型鋰離子電容於1C條件下循環10,000圈後，容量維持率達87％，庫倫效率＞99％，展現優異循環穩定性與電化學可逆性。

應用範圍

鋰離子電容製造、超級電容器、功能性複合材料與膜材加工等。

接受技術者具備基礎建議（設備）

電池塗佈與滾壓成型設備、Roll-to-Roll薄膜連續成型設備。

接受技術者具備基礎建議（專業）

具備化工材料、機械工程、電池生產製造等相關學經歷者。