建立一套適用於海上及臨海型太陽光電系統之「支架與鎖固材料耐腐蝕評估與驗證方法」，結合國際標準鹽霧循環試驗與實際海洋大氣曝露試驗，系統性評估不同金屬材料、鍍層與塗裝於極端高腐蝕（CX）環境下之耐久性與失效風險，作為材料選用與設計壽命評估之依據。

Abstract

This technology establishes an integrated corrosion evaluation and verification methodology for mounting structures and fastening materials used in offshore and coastal photovoltaic systems. By combining standardized cyclic salt mist tests with real-site marine atmospheric exposure, the approach systematically assesses the durability and failure risks of metals, coatings, and surface treatments under extremely high corrosivity (CX) environments, providing a basis for material selection and service-life design.

技術規格

•適用標準：IEC 60068-2-52（Test Method 8）、IEC 61701 Ed.3.0、ISO 9223、ISO 9226、CNS 13401 •試驗環境：酸性鹽霧（pH 3.5 ±0.1）、濕乾交替循環 •測試週期：10 週（約 1,680 小時，210 循環） •評估指標：外觀腐蝕分級、紅鏽／白鏽生成、鍍層劣化趨勢、腐蝕等級判定

Technical Specification

• Standards: IEC 60068-2-52 (Method 8), IEC 61701 Ed.3.0, ISO 9223, ISO 9226, CNS 13401 • Environment: Acidic cyclic salt mist (pH 3.5 ±0.1) with wet–dry cycles • Test duration: 10 weeks (about 1,680 hours, 210 cycles) • Evaluation metrics: corrosion appearance grading, red/white rust formation, coating degradation, corrosivity classification

技術特色

• 已完成實驗室加速試驗與澎湖實場海洋大氣曝露驗證 • 證實澎湖臨海場址對碳鋼、銅、鋁屬於 ISO 9223 之 CX 極端高腐蝕環境 • 建立不同鎖固與支架材料在 CX 環境下之耐蝕排序與失效型態 • 技術成熟度：TRL 6–7（系統級驗證完成，可供工程導入）

應用範圍

太陽光電系統建置規劃與評估。