技術簡介

藉由改變環狀嵌段共聚高分子(Cyclic block copolymer, CBC)與乙烯-醋酸乙烯共聚物(Ethylene-vinyl acetate copolymer, EVA)之混和比例混合，開發出特性符合製程需求之耐高溫緩衝層材料。並且結合開發的耐高溫緩衝層材料與自主新型疊片模組專利，封裝成1700*1000 mm之模組及驗證新型疊片模組的耐壓強度，實驗結果顯示新型疊片模組的Pmax為333.57W。將新型疊片模組進行靜態機械負荷測試，其模組功率損失為0.46％，符合規範IEC61215規定之小於初始功率的5％。

Abstract

High temperature resistant buffer layer material which the characteristics meet the requirements of the manufacturing process was developed by changing the mixing ratio of the cyclic block copolymer (CBC) and the ethylene-vinylacetate copolymer (EVA). The compressive strength of the new type shingled module with the patent of the high-temperature buffer layer material was verified. And it was encapsulated into a 1700*1000 mm module. The experimental results show that Pmax of the new type shingled module is 333.57W. After static mechanical load test (SMLT), the power decayed of the new type shingled module is 0.46％. The result fit the IEC standard 61215, the power decayed lower than 5％ of the initial value.

技術規格

1. 疊片模組技術 2. 緩衝層 3. 緩衝層以環狀嵌段共聚高分子與乙烯-醋酸乙烯共聚物混摻而成 4. 裂解溫度(Td5％，℃) Td≧310℃ 5. 熔融指數(g/10min) ＞400 6. 軟化融解溫度：≦ 190 ℃ 7. 黏度≦2000 cps

Technical Specification

1. shingled module technology 2. buffer layer 3. buffer layer mixing with cyclic block copolymer (CBC) and the ethylene-vinyl acetate copolymer (EVA) copolymer 4. thermal decomposition temperature (Td5％) Td≧310℃ 5. melt index (g/10min), MI ＞400 6. softening point ≦ 190 ℃ 7. viscosity≦2000 cps

技術特色

疊片式太陽光電模組是將太陽能電池切成條狀，並將它們以堆疊方式串接，消除了電池間間隙，可以將更多的矽電池片放置於一個模組中，從而提高模組輸出功率和模組效率。本技術新型疊瓦模組技術，有別於傳統導電膠式串接疊片模組技術，它保留原有焊帶串接及利用緩衝層解決電池片疊片處應力破片問題，同時達到高效模組目的，差異化之新型疊片模組技術。

應用範圍

太陽光電模組

接受技術者具備基礎建議（設備）

串焊設備

接受技術者具備基礎建議（專業）

太陽光電模組封裝製程